The copolyester of polyethylene terephthalate (PET) containing polyethylene glycol (PEG) unit was prepared by melt polycondensation process and its solid state polycondensation process was studied. The composition of copolyester was determined by NMR spectroscopy. In solid state polycondensation, the overall reaction rate was governed by the reaction temperature, initial molecular weight and PEG contents in copolyester. The contents of carboxyl end group was decreases during solid state polycondensation. The change of crystal structure by the stolid state polycondensation was not observed but the crystallinities were increased with the increase of reaction rate. By the solid state polycondensation, double melt endotherm peaks were appeared and discussed.

Polyethylene glycol (PEG)를 함유하는 polyethylene terephthalate(PET)의 공축합체를 용융축중합반응으로 합성하고 이의 고상중합반웅응 조사하였다. 합성한 공축합체의 조성은 핵자기 공명 분석으로 공축합체등의 PEG함량을 정량하였다. 고상중합속도는 반응온도, 초기 분자량 및 공축합체중의 PEG함량에 각각 의존하였고 카르복시 말단기 수는 고상중합의 시간에 따라 감소하는 경향을 보였다. 또한 고상중합에 의하여 결정구조의 변화는 없었으나 결정화도는 증가하는 현상을 보였다. 고상중합체의 융점(Tm)은 두 개의 peak로 나타났고 반응시간이 길어짐에 따라 한 개의 peak로 모여졌으며 이들의 원인을 검토하였다.

Keywords: