To prepare flame retardant acrylonitrile(AN) copolymers, AN was radically copolymerized with 2,4,6-tribromophenyl acrylate(TBPhA) and big(β-chloroethyl )vinyl phosphonate(CEVP) in benzene and the copolymerization reactivity ratios were determined. Thermal stabilities were measured by thermogravimetric analysis(TGA) and it was found that the increase of the comonomer contents decreased the thermal stabilities of the copolymers. In limit oxygen index(LOI) measurements the copolymers showed selfextinguishability when their THPhA or CEVP content reached 32wt.% or 47wt.%, respectively. When the contributions to the LOI of the flame retarding elements in CEVP, phosphorus and chlorine, a synergistic effect between the two elements could be detected.

Acrylonitrile(AN)수지의 난연화 연구를 위해 난연화 기능이 있는 2,4,6-tribromophenyl acrylate(TBPhA)와 bits(β-chloroethyl)vinyl phosphonate (CEVP)등의 단량체들과 AN단량체를 2,2''-azobisisobutyronitrile(AIBN)을 촉매로 60℃의 benzene 용액에서 공중합시키고 공중합 반응성비를 측정하였다. 얻어진 AN 공중합체 의 열안정성을thermogravimetric analysis(TGA)로 살펴본 결과 AN공중합체중의 TBPhA 및 CEVP함량이 늘어감에 따라 homopoly(AN)보다 더욱 나빠짐을 보였다. Limit oxygen index(LOI)에 의한 난연효과 실험에서는 AN 공중합체 내에 TBPhA및 CEVP가 삭각 32wt.%및 47w4.%가 되었을때 자소성을 보였으며 각 단량체의 난연화 원소들만의 무게 분율을 서로 비교했을 때는 CEVP중에 있는 염소와 인 사이에는 난연화 상승효과가 있는 것으로 판단되었다.

Keywords: