The thermal properties or crystallinity of poly(ethylene terephthalate) (PET) modified by 1,2-propane diol(1,2-PD) unit or 1,3-propane diol(1,3-PD) unit were studied. Glass transition temperature (T_g), melting temperature(T_m), crystallinity, and crystallization rate near T_m were decreased by the added 1,3-PD unit, but the crystallization rate near 79 was increased by the added 1,3-PD unit. In the case of PET modified by 1,2-PD unit, T_g was slightly increased, T_m or crystallinity was decreased more than that by 1,3-PD unit, and crystallization rate was decreased at all temperature range by the added 1,2-PD unit. Above results show that the 1,3-PD unit which does not crystallize improves the flexibility of main chain, but the 1,2-PD unit which also does not crystallize reduces the flexibility of main chain.

PET에 제3의 단량체로 1,2-PD 혹은 1,3-PD를 도입한 copolyester플 합성하여 조성을 핵자기 공명 분석으로 확인하고 조성에 따른 열적 성질과 결정화도의 변화를 조사하였다. 1,3-PD의 함량이 증가함에 따라 copolyester의 T_g, T_m, 결정화도는 감소하는 경향을 보였으며 결정화 속도는 T_m부근에서는 지연되었으나 T_g부근에서는 오히려 증가되는 경향을 보였다. 한편 1,2-PD의 경우는 그 함량이 증가함에 따라 T_g는 조금 증가하는 경향을 보였고, T_m, 결정화도는 1,3-PD의 경우 보다 크게 감소 하였으며 결정화 속도는 T_g, T_m 부근에서 모두 크게 지연되는 경향을 보였다 이러한 결과는 1,2-PD, 1,3-PD 모두 결정화 할 수 없는 부분으로 작용하나 1,2-PD는 주쇄의 유연성을 감소시키는데 비해 1,3-PD는 주쇄의 유연성을 오히려 증가시킴을 보여준다.

Keywords: