An electrical conducting polymer, polypyrrole, has been electro-chemically Polymerized in the presence of tetrabutyl ammonium perchlorate or tetrabutyl ammonium fluoroborate as an electrolyte. The weight of polypyrrole on the Positive electrode increased linearly with the reaction time but did parabolically when the positive electrode was coated with Poly (vinyl chloride); The electrical conductivity of polypyrrole grown in Poly(vinyl chloride) showed 10^-2S/cm while the conductivity of the polymer formed directly on the Platinum was 1.OS/cm. The surface of the polypyrrole film facing the opposite electrode has completely different structure from the surface contacting the electrode. The polymer revealed a possibility of being used as a battery material showing a potential of 1.6 volt when it wag discharged.

전기전도성 고분자의 하나인 Polypyrrole 을 tetrabutyl ammonium Perchlorate혹은 tetrabutyl ammonium fluoroborate 를 전해질로 사용하여 전기화학적으로 중합하였다. (+)전극상의 Polypyrrole 의 중합량은 반응시간에 대해서 직선적으로 증가하였고, (+)전극이 PVC film 으로 도포되어 있을 경우에는 포물선과 같이 증가하는 경향을 나타내었다. PVC film 에서 자라난 Polypyrrole 의 전기전도도는 10S/cm 이었토 백금 전극 위에서 직접 중합된 Polypyrrole 의 전기전도도는 1.O^-2S/cm 이었다. 상대전극을 향하고 있는 Polypyrrole 의 표면구조는 반응전극과 접한 면의 구조와 다르게 나타났다. 이 고분자는 방전시 1.6 volt 의 전압을 내는 것으로 보아 전지로서의 사용가능성을 나타내고 있다.

Keywords: