In (±45°)_2S angle-ply tensile specimens, the high sheer stress acting on planes parallel to the fiber directions, the matrix characteristics controll the mechanical responses. To know these effects for the mechanical behavior and damage development, two different matrix systems, brittle matrix of 5208 and ductile matrix of 914, are investigated at several stress rates. The matrix nature changes the mechanical behavior and the damage development in these materials. The stress rates change the maximum stress at failure about 12% in T300/5208 and about 10% in T300/914. In T300/914 the fiber rotation displays an important role in large deformations. The maximum failure stress criterion is not very applicable for the systems with matrix controlled mechanical response.

Angle ply laminates(±45°)_2S의 인장실험에 있어서 shears stress에 의한 매트릭스 수지의 변형이 상기 구조의 기계적 행태를 좌우한다. 수지의 특성에 따른 변화를 살펴보기 위하여, brittle한 5208수지와 ductile한 914수지를 사용하여,그 행태를 stress rate를 변화시켜가며 조사하였다. Stress rate에 의한 파괴시 최대 stress의 변화는 운300/5208의 경우 12%, T300/914의 경우는 10%였다. T300/914의 경우에 변형이 커짐에 따라 fiber rotation에 의한 영향이 나타남을 알 수 있었다. 상기구조에 대한 maximum failure criterion의 적용은 많은 문제점을 수반할 것으로 여겨진다.

Keywords: