  • Reverse Osmosis of Alginic Acid-Copper(Ⅱ) Complex Membranes
  • Kim JH, Kim KY, Tak TM
  • 구리이온 가교화 알긴산 막의 역삼투
  • 김정훈, 김계용, 탁태문
Abstract
Aqueous 6 wt% sodium alginate solution was prepared, which was cast onto glass plate and dried under constant temp. After this, the glass plate covered with the sodium alginate membrane was dipped into aqueous Cu(NO3)2·3H2O solution in order to prepare alginic acid-copper(Ⅱ) complex membrane. From the reverse osmosis experiments of these membranes. permeation characteristics of ionic solution were consistent with Donnas exclusion principle and these membranes were suitable for the desalination of low concentration salt solution. The membrane of 29㎛ thickness had a salt rejection of 88% and flux of about 8.0×10-3ml,/min·cm2 at 60 atm in 0.01 M NaCl solution.

알긴산나트륨을 물에 녹여 6wt%수용액을 만들고 이를 유리판위에 일정두께로 부은 후 상온에서 완전건조시켰다. 그후 Cu(NO3)2·3H3O 수용액에 침지시켜 구리이온가교화 알긴산막을 제조하였다. 실험결과로부터 역삼투특성은 Donnan 배제이론과 잘 일치하고 있었으며 이러한 막은 저농도의 탈염에 적합하다는 것을 알 수 있었다. 60기압, 막두께 29㎛에서 0.01M NaCl의 경우 88%의 rejection과 8.9×10-3cc/min·cm2의 flux를 나타냈다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1987; 11(3): 254-260

    Published online Jun 25, 1987

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: