The importance of fire safety in public transportation has been increased. Among interior materials vulnerable to fire, cushion materials made of polymer-based foam require high flame retardancy due to toxic gas generation and secondary propagation of flames. Since the silicone foam impregnated with the flame-retardant filler changes its mechanical properties, a mechanical reliability analysis was performed on it. In order to predict the mechanical behavior of hyperfoam, finite element analysis was performed using the Ogden model. In addition, parameters were obtained through an optimization process in consideration of the viscoelastic properties of the specimen, and the transmissibility according to the external vibration frequency were analyzed. As a result, it was observed that the external vibration frequency had a high transmittance of 1 or more between 5 and 15 Hz, while exhibiting a transmittance of 1 or less at frequencies of 5 Hz or less and 20 Hz or more.

대형 수송기기에서의 화재 안정성에 대한 관심은 나날이 높아지고 있다. 화재에 취약한 내장재 중에서도 특히 고분자 기반의 발포체로 이루어진 방석재는 유독 가스 발생 및 화염의 2차 전파 등의 이유 때문에 높은 난연성이 요구된다. 하지만 난연 필러가 함침된 실리콘 폼은 기계적 성질이 변하므로 이에 대한 기계적 신뢰성 분석을 실시하였다. 이를 위해 초탄성 물질의 기계적 거동을 예측할 수 있는 Ogden 모델을 활용하여 유한요소해석을 수행하였다. 또한 시편의 점탄성 특성을 고려하여 최적화 과정을 통해 파라미터를 얻고, 전달률 실험을 통해 외부 진동 주파수에 따른 전달률 특징을 분석하였다. 그 결과, 외부 진동 주파수가 5-15 Hz 사이에서 1 이상의 높은 전달률을 가지는 반면 5 Hz 이하, 20 Hz 이상의 주파수에서 1 이하의 전달률을 나타내는 것을 관찰할 수 있었다.

Keywords: hyper-foam, flame retardant, silicone foam, Ogden model, transfer.