Surface modification of nano silica was carried out using fluorine and acrylate. The physical properties of coated films were characterized. C-F and C=C absorption band of FTIR spectra confirmed that hydroxyl groups on the surface of nano silica was substituted by fluorine and acrylate, respectively. A noticeable increase in contact angle on coated surface was found due to the appearance of fluorine on coated surface by hybrid UV crosslinking between nano silica and acrylate coating material. It was expected that this hydrophobic surface may result in good anti-stain properties. In addition, the hardness of surface was also improved by modified nano silica. This means that the developed organic/inorganic hybrid coating material has multi-functional characteristics to enhance both anti-stainand hardness as well.

나노실리카 표면을 아크릴레이트와 불소기로 개질하여 다기능 유무기하이브리드 하드 코팅액을 제조하고 이들 코팅막 물성 변화를 살펴보았다. FTIR 확인 결과, 개질된 나노 실리카는 C-F와 C=C 흡수피크를 가짐으로 표면이 불소기와 아크릴레이트기로 개질되었음을 알았다. 개질된 나노실리카가 첨가된 아크릴레이트 하드 코팅제를 광경화시킨 경우, 나노실리카와 아크릴레이트 코팅제의 광 결합에 의하여 나노실리카 표면 불소기가 코팅도막 표면에 존재하여 코팅막 접촉각이 현저히 증가하여 우수한 내오염성을 가질 것으로 예측된다. 아울러 표면 경도 또한 증가하여 고경도와 내오염성 모두를 증가시키는 다기능 유무기하이브리드 코팅제를 제조하였다.

Keywords: nano silica; modification; multi-functional organic/inorganic hard coating; anti-stain; pencil hardness