A new inverse emulsion polymerization process was developed to synthesize po1yvinylpyrrolidone. Development of the process was emphasized on obtaining maximum molecular weight varying reaction conditions in terms of reaction temperature, reaction time, initiator, emulsifier, and reducing agent. Two redox systems were tested and molecular weight was measured by intrinsic viscosity and the Mark- Houwink equation. Reducing agent NaHSO₂·CH₂O gave higher molecular weight than NaHSO₃ at 30℃ reaction temperature and 2.5 hrs. reaction time. Existence of maximum molecular weight in concentrations of initiator, emulsifier, and reducing agent implies that PVP polymerization does not follow the ideal emulsion polymerization mechanism.

역유화중합법에 의해 N-vinylpyrroline을 합성하여 polyvinylpyrrolidone(PVP)을 얻는 새로운 공정을 개발하였다. 공정의 개발은 최대의 분자량을 주는 반응조건의 확립에 중점을 두고, 반응온도, 반응시간, 개시제, 유화제, 환원제의 분자량에 대한 영향을 검토하였다. 두 산화일환원촉매계를 사용하였고, 분자량의 측정은 고유점도의 측정과 Mark-Houwink식에 의해 계산하였다. 환원제 NaHSO₂·CH₂O가 NaHSO₃보다 높은 분자량을 주었고, 반응온도 30℃, 반응시간 2.5시간일 때 가장 높은 분자량을 얻었다. 개시제와 유화제, 환원제는 최대의 분자량을 주는 농도를 보여주어, PVP의 중합은 이상적인 유화중합기구에서 벗어나고 있다.

Keywords: