The crystallization kinetics of Nylon 66 were studied by the depolarized light intensity method. The effects of crystallization temperature, molecular weight, and sodium phenylphosphinate (as a nucleating agent) concentration on the rate of crystallization were evaluated. Avrami equation was used for the determination of the overall rate of crystallization, t_1/2^-1. In the temperature range of 232-243℃, the overall rate of crystallization, t_1/2^-1 varied from 0.0435 to 0.0125, and Avrami exponent, n were about 3-4. The overall rate of crystallization varied from 0.0164 to 0.0204 as the number average molecular weight decreases from 16,500 to 15,500. This overall rate of crystallization was comparable to a commercial injection molding grade Nylon 66, Leona 1300S. The overall rate of crystallization varied from 0.0172 to 0.0278 in the presence of 1wt% sodium phenylphosphinate as a nucleating agent. The Avrami exponent, n varied from 11.8 to 3 in the presence of 1wt% sodium phenylphosphinate.

탈편광 광도법에 의해 나이론 66의 등온 결정화 속도를 측정하여, 결정화온도, 분자량, 기핵제 등의 결정화 속도에 미치는 영향을 검토하였다. 헥사메틸디아민과 아디프산으로부터 중합된 나이론 66과 Leona 1300S(일본 Asahi사 제품)를 시료로 사용하였으며, 기핵제로는 페닐프스핀산염을 사용하였다. 개미산 용액으로부터 film을 제조하여 이를 결정화 속도 측정에 사용하였다. 얻어진 결과는 Avrami equation을 이용하여 해석하였으며, 그 결과는 다음과 같았다. 결정화 온도 범위 232∼243℃에서 총괄 결정화 속도 t_1/2^-1은 0.0435에서 0.0125의 값을 취하고, Avrami지수 n은 약3∼4이었다. 수평균 분자량이 16,500에서 15,500으로 감소할 때, 총괄 결정화 속도 t_1/2^-1은 0.0164에서 0.0204로 증가하였다. 이 총괄 결정화 속도 값은 상업화된 사출 성형 규격의 나이론 66인 Leona 1300S에 견줄만한 값이었다. lwt% 페닐프스핀산염이 존재할 때 총괄 결정화 속도는 0.0172에서 0.0278로 증가하였으며 Avrami지수는 11.8에서 3으로 감소하였다.

Keywords: