α,ω-Hydroxypropyl polydimethylsiloxane (HO-PDMS) was prepared by hydrosilylation of hydrogen terminated polydimethylsiloxane with allyl alcohol. Polydimethylsiloxane modified urethane with isocyanate group (PSU) was prepared from cyclic trimer of hexamethylenediisocyanate with HO-PDMS. PDMS modified urethane base resin with acrylic group (PSUA) was prepared from the urethane reaction of PSU with isocyanate group and 2-hydroxyethylmethacrylate. Their structures were characterized using FTIR and NMR. Coating materials were prepared by mixing PSUA, acrylic hardner, photo-initiator, and solvent and coated on PET film to obtain flexible and hard coating film by UV irradiation. Transparency of coating film was 89.7%, contact angle, 88°, and pencil hardness, 3H.

α,ω-Hydroxypropyl기를 갖는 polydimethylsiloxane을 합성하고 이를 hexamethylenediisocyanate(HDI)의 고리화 반응으로 제조된 HDI trimer와 반응시켜 말단에 이소시아네이트 기를 갖는 PDMS 변성 urethane(PSU)을 제조하였다. 이소시아네이트기를 갖는 PSU와 2 - hydroxyethylmethacrylate를 urethane 반응으로 acrylate기를 갖는 PDMS 변성 urethane base 수지(PSUA)를 제조하였으며, 이를 FTIR, NMR로 구조를 확인하여 분석하였다. 제조한 base 수지에 아크릴계 경화제, 광 개시제, 용매들을 혼합하여 코팅 액을 제조하였으며 이를 PET 필름에 도포하고 자외선으로 조사하여 고경도의 유연성을 갖는 코팅 막을 얻었다. 얻어진 코팅 막의 광 투과도는 89.7%, 연필경도는 3H, 접촉각은 88° 였다.

Keywords: hydroxypropylpolydimethylsiloxane; hexamethylenediisocyanate; coating material; pencil hardness.