Soap-free emulsion copolymerization of styrene and acrylonitrile was carried out by use of potassium persulfate-sodium, bisulfite redox initiator. Effects of initiator concestraction, monomer to water ratio, monomer feed ratio and polymerization temperature on the rate of polymerization were investigated. It was found that the conversion increased with initiator concentration, the ratio of monomer to water, the concentration of acrylonitrile in the feed and polymerization temperature. The overall activation energy for the copolymerization was determined to be 11.8 ㎉/mole from the Arrhenius plot. The content of acrylonitrile in the copolymers increased with the ratio of monomer to water and the concentration of acrylonitrile in the monomer mixture.

유화제부재하에서 potassium persulfate-sodium bisulfite 계의 redox 개시제를 사용한 styrene과 acrylonitrile의 유화공중합을 실시하여 개시제의 농도, 단량체의 혼합비, 중합온도 및 물의 함량이 중합수율과 공중합체의 평균조성에 미치는 영향을 검토하였다. 중합수율은 개시제의 농도, 단량체 혼합계내에서 acrylonitrile의 함량 및 물에 대한 단량체의 중량비가 증가할수록 증가하였으며, 생성된 공중합체중의 acrylonitrile 조성은 물에 대한 단량체의 중량비에 따라 증가하였다.