  • Synthesis of Biodegradable Aliphatic Polyester with Amino Group in the Side Chain
  • Lee CW
  • 곁사슬에 아미노기를 도입한 생분해성 지방족 폴리에스테르의 합성
  • 이찬우
Abstract
Aiphatic diester monomer, 3-[(benzyloxycarbonylamino)butyl]-1,4-dioxane-2,5-dione (BABD), was synthesized with the N-ε-benzyloxy-carbonyl-L-lysine as starting material. This monomer was synthesized to add the functionality to poly(lactic acid)s. BABD unit was successfully incorporated into the PLLA chain which was confirmed by 1H NMR. The copolymer composition could be controlled by the feed ratios of monomer. The Mn of this resultant polymer is expected to reach high molecular weight after the purification of monomer and optimization of polymerization time, though the polymer showed relatively low degree of polymerization (Mn=3300). The copolymer is expected to possess the enhanced hydrophilicity and the possibility of chemical modification on amino group.

Poly(lactic acid)계 고분자의 기능화를 목적으로 곁사슬에 아미노기를 도입한 지방족 폴리에스테르를 합성하고자 하며, N-ε-benzyloxy-carbonyl-L-lysine을 출발물질로 한 디에스테르 단량체 3-[(benzyloxycarbonylamino) butyl]-1,4-dioxane-2,5-dione(BABD)를 합성하였다. BABD와 L-lactide와의 공중합의 결과, PLLA 사슬에 BABD단위가 도입된 것이 확인되었으며 공중합체의 조성은 단량체의 첨가량에 따라 제어가 가능함을 알 수 있었다. 얻어진 폴리머는 Mn=3300 정도로 낮은 중합도를 나타내었으나 단량체의 정제 및 중합시간의 검토에 의해 고분자량체의 생성이 가능함을 확인하였다. 곁사슬에 아미노기를 도입함에 의해 얻어진 폴리머는 친수성의 향상, 아미노기에 대한 화학수식 등에 의해 기능성의 부여가 기대된다.

Keywords: aliphatic diester monomer; functionality; copolymerization; feed ratio; hydrophillicity

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2010; 34(4): 381-385

    Published online Jul 25, 2010

  • 10.7317/pk.
  • Received on Apr 28, 2010
  • Revised on Nov 30, -0001
  • Accepted on Jun 16, 2010

Correspondence to

  • E-mail: