Poly(N-isopropylacrylamide)(PNIPAAm) containing polydimethylsiloxane(PDMS) block and nano clay was obtained by the polymerization of NIPAAm and [3-(methacryloylamino)propyl]trimethyl ammonium montmorillonite(MAPTAC-MMT) with PDMS-macroinitiator. The polymer was characterized with FT-IR, XRD and DSC. The addition of PDMS in the polymers did not affect the value of the lower critical solution temperature(LCST) and the glass transition temperature(Tg) of the PNIPAAm. However, the swelling ratio decreased with increasing PDMS contents. In the case of PNIPAAm containing nano clay, the content of MAPTAC-MMT did not affect swellability, but the Tg of the PNIPAAm decreased with increasing nano clay contents.

Polydimethylsiloxane(PDMS) macroinitiator를 이용하여 N-isopropylacrylamide(NIPAAm)와 [3- (methacryloylamino)propyl]trimethyl ammonium montmorillonite(MAPTAC-MMT)를 중합하여 주사슬에 PDMS 블록을 가지며 nano clay(montmorillonite)를 가진 PNIPAAm 중합체를 합성하여 FT-IR과 XRD를 이용하여 확인하고 DSC를 이용하여 열적 성질을 조사하였으며 중합체의 온도에 따른 수팽윤도를 구하였다. DSC 측정 결과 poly(NIPAAm-b-PDMS) 속의 PNIPAAm과 PDMS는 분리된 상으로 존재했으며, 소수성인 PDMS의 함량이 증가함에 따라 수팽윤도는 감소하였으나 LCST 값은 큰 변화가 없었다. 또한, PNIPAAm의 유리전이온도 (Tg)는 분리된 상으로 인해 큰 변화가 없었다. 또한, 나노입자의 첨가는 전반적으로 수팽윤도에는 영향을 주지 않았으나 중합체의 Tg의 값은 감소하였다.

Keywords: N-isopropylacrylamide; montmorillonite; polydimethylsiloxane; thermo-reversible; swelling