  • Strength and Durability of Polymer Modified Mortar according to Monomer Ratio of Methyl Methacrylate and Butyl Acrylate
  • Mun KJ, Hyung WG
  • MMA/BA의 단량체 비에 따른 폴리머 시멘트 모르타르의 강도 및 내구성
  • 문경주, 형원길
Abstract
The purpose of this study is to clarify the effect of the monomer ratio on properties of the polymer-modified mortars using methyl methacrylate-butyl acrylate(MMA/BA) latexes, and to obtain basic data necessary to develop appropriate latexes for cement modifiers. From the test results, the total pore volume of polymer-modified mortars using MMA/BA latexes is linearly reduced with an increase in the bound MMA content and increased in the polymer-cement ratio. In general, the superior flexural and compressive strength of polymer-modified mortars using MMA/BA latexes is obtained at a bound MMA content of 70 or 80 percent and a polymer-cement ratio of 15%. And, the water absorption and chloride ion penetration depth are greatly affected by the polymer-cement ratio rather than the bound MMA content.

본 연구에서는 MMA(methyl methacrylate)와 BA(buthyl acrylate)를 단량체로 이용한 폴리머 시멘트 모르타르의 단량체 비에 따른 성질을 파악하고 시멘트 혼화용 폴리머로 활용하기 위한 기초적 자료를 얻고자 하였다. 본 연구결과 MMA/BA를 이용한 폴리머 시멘트 모르타르의 전 세공용적은 MMA/BA의 단량체 비가 증가할수록 감소하는 것으로 나타났다. 강도특성에서는 전체적으로 MMA/BA의 단량체 비가 70:30, 그리고 80:20일 때, 폴리머 시멘트 비가 15%일 때 가장 우수한 증진효과를 나타냈다. 폴리머 시멘트 모르타르의 내구성을 측정하는 흡수율, 염화물 이온 침투 저항성, 중성화 저항성에서는 단량체 비에 따른 개선보다는 폴리머 시멘트 비에 따른 개선효과가 더 큰 것으로 나타났다.

Keywords: polymer; monomer ratio; synthesis; polymer-modified mortar; porosity

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2008; 32(6): 603-609

    Published online Nov 25, 2008

  • 10.7317/pk.
  • Received on Aug 21, 2008
  • Revised on Nov 30, -0001
  • Accepted on Sep 17, 2008

Correspondence to

  • E-mail: