Two kinds of colloidal silica(CS)/silane sol solutions were prepared in variatin with synthesizing parameters such as kinds of CS, ratio of CS to silane and reaction time. Such sol solutions were obtained from 1034A CS/methyl-trimethoxysilane(MTMS) and HSA CS/MTMS solutions. In the case of 1034A CS/MTMS CS/silane sol, coating film had high contact angle and more enhanced flat surface than those in the case of HSA CS/MTMS sol. In the case of thermal stability, thermal dissociation of 1034A CS/MTMS sol did not occur up to 550 ℃. The thickness of coating film obtained from 1034A CS/MTMS sol invreased with increasing the amount of MTMS. The hardness of coating films obtained from 1034A CS/MTMS sol decreased with increasing the amount of MTMS. Surface free energy of CS/silane sol-gel coating film decreased with increasing amount of MTMS.

콜로이드 실리카 종류, 콜로이드 실리카/실란의 함량비, 반응시간 등의 반응조건에 따라 두 종류의 콜로이드 실리카/실란 솔을 합성하였다. 이러한 졸을 이용하여 솔-젤 코팅막을 제조하여 물리적 화학적 특성을 조사하였다. 그 결과 1034A 콜로이드 실리카계로부터 얻어진 솔-젤 코팅막의 접촉각과 표면균질성은 HSA계 솔-젤 코팅막에 비하여 우수하였다. 그리고 1034A 콜로이드 실리카계로부터 얻어진 솔-젤 코팅막은 550 ℃까지 열분해없이 안정하였고 methyltrimethoxysilane(MTMS) 함량이 증가할수록 코팅막의 두께가 두꺼워 졌다. 1034A 콜로이드 실리카계 솔-젤 코팅막의 경도는 MTMS의 함량 증가에 따라 감소하였으나 HSA계는 큰 영향을 받지 않았다. 표면에너지는 MTMS 함량 증가와 더불어 전반적으로 감소하는 경향을 보였다.

Keywords: sol-gel; colloidal silica; tetramethoxysilane; methyltrimethoxysilane; coating film