Polystyrene particles (PS) with poly(ethylene glycol) units on surface were formed by an emulsifier-free emulsion polymerization using styrene, poly(ethylene glycol) methacrylate (PEG-MMA) or poly(ethylene glycol) dimethacrylate (PEG-diMMA) at pH 7, and followed by freeze-drying to give the corresponding powders. The structures of PS particles were confirmed by FT-IR spectroscopy, and the particle size and distribution the PS particle were observed by scanning electron microscopy and particle analyzer. Monodisperse polymer particles were obtained at a concentration of PEG-MMA 2~5 mol% or PEG-diMMA 1 mol% relative to styrene. The highest zeta potential of polymer surface was measured to be 183 mV at a polymer of PEG-MMA 5 mol%, which was measured in dielectric medium by means of ELS-8000 dynamic light scattering.

스티렌, 폴리(에틸렌 글리콜) 메타크릴레이트 (PEG-MMA) 혹은 폴리(에틸렌 글리콜) 디메타크릴레이트 (PEG-diMMA)를 중성 매질에서 무유화제 (emulsifier-free) 유화 중합하여 표면에 에틸렌 글리콜기를 갖는 폴리스티렌 입자를 합성하였고, 이로부터 동결 건조되어진 분말을 제조하였다. 고분자 분말은 FT-IR 분광기로 구조를 확인하였고, 광산란 입도 분석기와 주사 전자 현미경 (SEM)을 이용하여 입자 크기와 분산도를 조사하였다. 스티렌에 대하여 공단량체 PEG-MMA는 2~5 mol%, PEG-diMMA는 1 mol% 농도 부근에서 균일한 입자 크기를 얻을 수 있었다. 합성된 입자의 표면 전하를 유전 매질 내에서 ELS-8000 광산란법을 이용하여 제타 포텐셜을 측정하였다. 스티렌에 대하여 PEG-MMA 5 mol%에서 183 mV의 아주 높은 제타 포텐셜이 측정되었다.

Keywords: emulsifier-free emulsion polymerization; poly(ethylene glycol) methacrylate; poly(ethylene glycol)dimethacrylate; polystyrene powders; zeta potential