Poly(trimethylene terephthalate) (PTT) fibers were treated by passing on the plate heater to study the annealing effect on the change of morphological structure and physical properties. In the X-ray diffraction curves of PTT annealed, a sharp peak at 2θ = 15.6° appeared and the peak intensity became stronger with the increase of annealing temperature and time. This peak was based on the (010) plane of PTT crystals. The crystallinity determined by density measurement was also increased by annealing. With the increases of temperature and time, the dynamic viscoelastic behaviors were shown to be a large reduction in T(tan δ_max). The birefringence and T_g were also reduced, but the melting temperature was the same. These results mean that the molecular chains in armorphous region are transfered into the crystalline region, making the remained chains relaxed during annealing at tensionless state.

연속순간 평판열처리가 폴리(트리메틸렌 테레프탈레이트) (PTT) 섬유의 미세구조 및 물성에 미치는 영향을 고찰하기 위해 열처리 온도 및 시간을 변화시키면서 PTT 섬유를 처리하였다. X-선 회절 분석 결과 적도선 방향에서 (010)면의 회절 피크가 2θ = 15.6° 에서 관찰되었으며, 열처리 온도 및 열처리 시간의 증가에 따라 X-선 회절 강도 분포 곡선은 예리해졌다. 또한 열처리 시료의 결정 크기 및 중량분율 결정화도도 열처리 온도와 열처리 시간의 증가에 따라 모두 증가하였다. 동적 점탄성 특성을 분석한 결과 열처리 온도 및 열처리 시간의 증가에 따라 T(tan δ_max)는 크게 감소하였으며, 복굴절률과 유리 전이 온도도 감소하였고, 용융 온도는 변화가 없었다. 이로부터 열처리 온도 및 열처리 시간의 증가에 따라 비결정 영역 중분자 사슬의 충전 밀도는 낮아지고, 분자 사슬은 긴장이 완화되는 것으로 생각되었다.

Keywords: poly(trimethylene terephthalate); plate heater annealing; crystallinity; morphological structure; physical properties