The crystallization characteristics of metallocene linear low density polyethylene was investigated by small angle light scattering and comparison was made with Ziegler-Natta linear low density polyethylene. The special efforts were made to find out the effects of branching number, length of branching and co-monomer content of m-LLDPE on the crystallization behavior of m-LLDPE. It was found that m-LLDPE has longer induction time to start crystallization from the amorphous state than that of conventional LLDPE with similar branching number, but the rate of crystallization seems not change much in both LLDPEs. Lowering of branching number in m-LLDPE resulted in both increasing of rate of crystallization and reducing induction time to crystallize. In general, the maximum size of spherulites of m-LLDPE is bigger than that of conventional LLDPE.

광산란 장치를 이용하여 메탈로센 촉매 하에 제조된 메탈로센 선형 저밀도 폴리에틸렌의 결정화거동을 Ziegler-Natta 촉매에 의하여 제조된 선형 저밀도 폴리에틸렌과 비교하여 보았다. 특히 branching 수와 길이 그리고 공단량체의 함량이 결정화 거동에 미치는 영향을 중점적으로 살펴보았다. 같은 수의 branching 수를 가지고 있는 메탈로센 선형 저밀도 폴리에틸렌은 기존의 선형 저밀도 폴리에틸렌에 비하여 결정화를 시작하기 위한 induction time이 길어짐을 알 수 있으나 구정의 성장속도는 두 경우가 유사함을 확인하였다. 메탈로센 선형 저밀도 폴리에틸렌의 branching 수를 감소시킬 경우 induction time과 구정성장속도가 모두 빨라짐을 알 수 있었다. 또한 일반적으로 최대 구정의 크기는 branching 수에 관계없이 메탈로센 선형 저밀도 폴리에틸렌이 기존의 선형 저밀도 폴리에틸렌에 비하여 커짐을 알 수 있었다.

Keywords: metallocene low density polyethylene; crystallization; branching number; small angle light scattering; induction time