The solvent extraction of polyethylene glycol(PEG) by ethanol has been studied for the powder injection molded compacts of Sr-ferrite/PEG/carnauba wax/HDPE. The extraction rate of PEG is sensitively proportional to the solvent temperature whereas it is inversely proportional to the contents of PEG, the molecular weight of PEG, and the specimen thickness. The high extraction rate of PEG is achieved under the following conditions: solvent temperature of 70 ℃, PEG contents of 30 %, and PEG molecular weight of 400 g/mol. In the early stage of solvent extraction, the non-linear relationship between the extraction rate and the square root of the extraction time indicates that the extraction of PEG does not follow the Fickian behavior. At extraction times longer than 180 min, however, the extraction of PEG follow the Fickian behavior. The extraction rate of PEG by ethanol is about 1.0 X 10(-6) g/cm(2)sec enough for common applications.

에탄올에 의한 폴리에틸렌글리콜(PEG)의 용매추출법이 Sr-페라이트/PEG/carnaubawax/HDPE로 구성된 분말사출성형체에서 연구되었다. 에탄올에 의한 PEG의 추출율은 용매의 온도에 민감하게 비례하나, PEG의 첨가량, PEG의 분자량, 그리고 시편의 두께에는 반비례한다. 에탄올에 의한 PEG의 효과적인 용매추출은 70 ℃의 용매온도, 30%의 PEG 첨가량, 400 g/mol의 PEG 분자량에서 가능하였다. 용매추출의 초기단계에서 에탄올에 의한 PEG의 추출율은 추출시간의 제곱근과 정비례관계를 갖지 않으므로 Fickian 거동을 나타내지 않는다. 그러나 180분 이상의 용매추출시간에서 PEG의 추출율은 Fickian 거동을 따른다. 에탄올에 의한 PEG의 추출속도는 상용화가 가능한 수준인 약 1.0 X 10(-6) g/cm(2)sec를 나타낸다.

Keywords: powder injection molding; solvent extraction; ethanol; polyethylene glycol(PEG)