  • Effect of Additives on the Orientation of Magnetic Sr-Ferrite Powders in Powder Injection Molded Compacts
  • Cho TS, Jeung WY
  • 분말사출성형체에서 Sr-페라이트 자성분말의 배향도에 미치는 첨가제의 영향
  • 조태식, 정원용
Abstract
The effect of additives on the orientation of magnetic Sr-ferrite powders has been studied during powder injection molding under applied magnetic field for fabricating multi-pole anisotropic sintered Sr-ferrite magnets. The orientation of the Sr-ferrite powders depends sensitively on the fluidity of powder-binder mixture, related to the binder additives and the injection molding temperature, and the magnetic field intensity. The orientation of Sr-ferrite powders is good for the compacts with stearic acid added in the binder system of paraffin wax/carnauba wax/HDPE, but it is poor for the compacts with silane coupling agent added. The orientation of Sr-ferrites higher than 80% is achieved at the following useful conditions; apparent viscosity lower than 2500 poise in 1000 sec(-1) shear rate and applied magnetic field higher than 4 kOe.

다극 이방성 Sr-페라이트 소결자석을 제조하기 위한 자장중 분말사출성형공정에서 Sr-페라이트 자성분말의 배향도에 미치는 결합제의 첨가제 영향이 연구되었다. 외부자기장의 방향에 대한 Sr-페라이트 자성분말의 배향도는 첨가제의 종류, 사출성형온도와 관련한 사출성형체의 유동성과 외부자기장의 세기에 크게 의존하였다. Paraffin wax/carnauba wax/HDPE 3성분계 결합제에 stearic acid를 첨가하면 분말사출성형체의 유동성이 향상되어 Sr-페라이트 자성분말의 배향도가 증가되었으나, silane계 커플링제를 첨가하면 성형체의 유동성이 오히려 감소되어 Sr-페라이트의 배향도가 감소되었다. 80% 이상의 Sr-페라이트 자성분말의 배향도는 사출성형체의 겉보기점도가 2500 poise(1000 sec-1)이하이고 외부자기장의 세기가 4 kOe 이상인 유용한 조건에서 얻어졌다.

Keywords: powder injection molding; orientation of Sr-ferrites; fluidity; stearic acid; coupling agent

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2001; 25(2): 240-245

    Published online Mar 25, 2001

  • 10.7317/pk.
  • Received on Nov 30, 2000
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: