The effect of petroleum resin as a tackifier for polyalphaolefin(APAO) hot melt adhesive on thermal prperties, crystallinity and adhesion strength was investigated. The presence of petroleum resin resulted in the melting temperature decrease in APAO/petroleum blend, especially, in APAO with low ethylene content/C₅ petroleum blend. It was also found that petroleum resin caused the decrease of crystallinity regardless of ethylene content in APAO. The maxium adhesion strength was found to be at 50/50(APAO/petroleum) composition. C₅ resin was more effective to increase adhesion strength than C₉ for APAO with high ethylene content. In addition, it was found that the adhesion strength was improved with the decrease of crystallinity in APAO/petroleum resin hot melts.

핫 멜트 접착제는 점착제로 사용되고 있는 석유수지를 비 결정성 올레핀 수지에 블렌딩하였을 때 점착제가 비 결정성 올레핀 수지의 열적 특성 및 결정화거동에 미치는 영향과 이에 따른 접착특성 변화에 대하여 살펴보았다. 점착제로 사용된 석유수지는 비 결정성 올레핀 수지의 용융온도를 저하시키고 이러한 현상은 에틸렌 함량이 상대적으로 많은 비 결정성 올레핀 수지에서 두드러지며, aromatic수지인 C₉ 석유수지보다는 aliphatic수지인 C₅ 석유수지를 사용할 때 그 감소의 폭이 큼을 알 수 있었다. 아울러 석유수지의 블렌딩에 의하여, 특히 aromatic수지인 C₉을 첨가하였을 경우, 비 결정서 수지의 에틸렌 함량이 적을수록 결정화도가 현저히 감소함을 확인할 수 있었다. 점착제의 조성비가 50% 정도에서 가장 우수한 접착력을 확인할 수 있었으며, 에틸렌 함량에 관계없이 C₅ 석유수지의 첨가시 접착력이 현저히 향상됨을 알 수 있었다. 에틸렌 함량이 적은 비결정성 올레핀/석유수지 핫 멜트에서는 점착제로 인하여 발현된 결정화도 감소에 의하여 접착특성이 증가됨을 알 수 있었다.

Keywords: hot melt adhesive; polyalphaolefins; petroleum resin; thermal properties; adhesion strength