Cure kinetics and rheological properties of diglycidylether of bisphenol A (DGEBA)/trimethylolpropane triglycidylether (TMP) epoxy blends mixed in varying proportion with 1 wt% N-benzylpyrazinium hexafluoroantimonate(BPH) as a thermal latent curing agent were investigated. Latent properties were investigated by measuring convesion as a function of reaction time using isothermal DSC method at 160 an 50 ℃. The cure activation energies (Eg) obtained by Kissinger method using dynamic DSCdata were higher in DGEBA/TMP mixtures than in pure DGEBA. Rhelogical properties of the blend system were investigated under isothermal condition using a rheometer. Cross-linking activation energy(Ec) was also determined from the Arrhenius equation based on gel time and curing temperature. As a result, the cross-linking activation energy showed similar behabior with that of Kissinger method and gelation time decreased with increasing TMP content, which could be resulted from higher activated sites by trifunctional epoxide groups and low viscosity of TMP.

잠재성 양이온 경화제인 N-benzylpyrazinium hexafluoroantimonate (BPH)를 1 wt%첨가한 diglycidylether of bispenol A (DGEBA)/timethylolpropane triglycidylether (TMP)에폭시 블렌드의 혼합 조성비에 따른 경화 동력학과 유변학적 특성에 대해 연구하였다. 블렌드 시스템의 잠재 특성은 등온 DSC를 이용하여 각각 160 ℃와 50 ℃의 반응온도에 시간의 함수로서 전화량을 구하여 측정하였다. 승온 DSC로부터 Kissinger 방법으로 결정된 경화 활성화 에너지 (Ea)는 DEGBA 단일 성분보다 DGEBA/TMP 혼합물일 경우 증가하였다. 블렌드 시스템의 유변학적 특성은 레오미터를 사용한 등온 실험을 통하여 측정하였다. 측정한 겔화 시간과 경화 온도를 Arrhenius 방정식에 적용시켜 가교 활성화 에너지 (Ec)를 구한 결과, Kissinger 방법에 의한 활성화 에너지와 유사한 경향을 나타내었다. 이로서 TMP의 함량 증가에 따라 빠른 겔화 시간이 나타남을 알 수 있었으며, 이는 세 개의 에폭사이드기에 의한 활성점 증가와 낮은 점도 등에 기인한다.

Keywords: epoxy blends; cationic latent catalyst; activation energy