The PSF-g-AAc copolymers were synthesized by the irradiational grafting of acrylic acid onto polysulfone membrane. The synthesis of copolymer was evidenced by the bands at 1720, 3100 cm^-1 in the FR-IR spectrm. The initial thermal degradation temperature of PSF-g-AAc copolymers was about 250 ℃. After the adsorption of metal ions of PSF-g-AAc copolymers, various types of morphology with small brain, lump and sponge shape were observed by SEM. The optimal time for the metal ion adsorption equilibrium on PSF-g-AAc copolymers was 24 hrs and their adsorption capacties increased in the order of Cu²⁺>Ni²⁺>>Co²⁺>Mn²⁺>. The adsorption capacities of PSF-g-AAc copolymers were not varied even after more than 10 times of regeneration.

방사선 전조사법을 이용하여 아크릴산을 polysulfone 막에 그라프트 반응시켜 PSF-g-AAc 공중합체를 합성하였다. 합성한 공중합체의 FT-IR 결과 1720, 3100cm^-1 부근에서 C=0, -OH에 대한 피크가 확인되었고, PSF-g-AAc 고중합체의 초기 열분해 온도가 250 ℃에서 나타났다. 금속이온 흡착후에 공중합체의 표면은 작은 혹, 좁쌀, 뇌형태 및 스펀지 형태 등이 관찰되었고, PSF-g-AAc 공중합체의 금속이온에 대한 흡착능의 최적시간은 24시간이었으며 동일 조건하에서의 흡착능은 Cu²⁺>Ni²⁺>Co²⁺>Mn²⁺의 순서로 Cu²⁺이온이 최대 흡착량을 나타내었다. 또한 PSF-g-AAc 공중합체는 10회 이상 흡착능의 변화없이 흡탈착이 가능한 흡착제임을 알 수 있었다.

Keywords: irradiation; grafting reaction; thermal stability; adsorption