Effect of solvents on pore characteristics of styrene-divinylbenzene copolymers was investigated experimentally. Toluene was usedas a good solvent, and n-heptane and 2-ethyl-1-hexanol as poor solvents. Divinylbenzene(DVB) was used for controlling crosslinkage. The specific surface area and pore volume of the copolymers were increased with decreasing the ratio of monomer to solvent content. In the copolymer with high DVB content, the specific area was increased with increasing the ratio of good solvent to poor solvent content. In the copolymers with low DVA content, pore polume and pore size distribution which depend on the kind of solvents due to the strcutral ifference in these sovents were decreased with the higher degrees of crosslinking. Applied solvents, having different affinities for the copolymers, lead to their morphology changes during polymerization.

스티렌-디비닐벤젠 공중합에의 기공 특성에 대한 용매의 영향을 실험적으로 고찰하였다. 공중합체의 제조시 팽윤제로서 toluene을, 침전제로서 n-heptane과 2-ethyl-1-hexanol을 사용하였다. 가교제로는 디비닐벤젠 (DVB)을 사용하였다. 단량체와 용매의 함량비에서 용매의 함량이 증가할수록 공중합체의 비표면적과 기공부피가 증가하였다. 높은 DVB 함량조건에서는 팽윤제/침전제의 함량비가 증가할수록 더 큰 비표면적을 나타냈다. 낮은 DVB 함량조건에서는 2-ethyl-1-hexanol과 n-heptanedml 구조적 차이에 의한 기공 부피 및 기공크기분포의 차이를 보였다. DVB함량이 증가할수록 용매의 구조적 차이에 의한 효과가 감소하였다. 중합반응에 사용된 용매들은 공중합체에 대한 각기 다른 상호작용 때문에 공중합체의 합성 반응시 구조적 특성에 다양한 영향을 미치는 것으로 나타났다.

Keywords: styrene-divinylbenzene; copolymer; porous structure; good solvent; poor solvent