Poly(styrene-g-EVA) were prepared by irradiation of EVA-styrene mixture in air atmosphere. The mixtures (the solution of ELVAX 40 in styrene and the swollen ELVAX 250 in styrene) were irradiated in the cobalt 60 source at 15-20℃ with an average dose rage of 5.04×10⁴ mrad./hr. The grafted EVA were characterized in terms of % graft, with the dose, concentration and mixture phase as reaction variables. The results of grafting reactions indicated that the reactivity of the radicals formed at backbone and pendant acetate group (α-position) of EVA exhibited the similar reactivities toward monomer styrene. The dose rate doesn''t affect on the polymerization rate but only on the initial induction lag of grafting reactions. The dependence of % graft on concentration and mixture phase is negligible, and these phenomena are believed to be due to the fact that the occluded growing chains in viscous matrix attribute to the reaction more than the diffusion variable does on irradiation reactions. It appears that the grafting reaction kinetics of EVA-styrene system is similar to that of linear PE-styrene system''s.

Styrene-EVA 혼합물을 공기 존재하에서 방사선 조사시켜 그라프트중합시켰다. 방사선원은 Co⁶⁰을 이용하였고 15-20℃에서 조사율은 5.04×10⁴ mrad/hr 로 고정시켰으며 생성된 그라프트중합체는 조사량, 혼합물의 조성 및 혼합물상을 변수로 하여 그라프트율 (% graft)을 측정하였다. 그라프트중합 결과 EVA의 주쇄와 아세테이트기 α-위치의 탄소에 생성된 라디칼은 styrene monomer에 대해 비슷한 반응성을 나타내고 조사율은 중합속도에는 영향을 미치지 않고 단지 초기 유도기간에만 영향을 나타낸다. 그라프트율은 EVA-styrene 혼합율 농도와 상에는 거의 영향을 받지 않는데 이 현상은 점조상의 반응혼합물 내에 흡장되어 있는 생성쇄가 반응에 미치는 영향이 단량체의 확산작용이 반응에 미치는 영향보다 크기 때문인 것으로 해석된다. 이상의 사실들로 보건대 EVA-Styrene 계의 그라프트중합은 PE-Styrene 계의 그것과 속도론적으로 비슷하다고 하겠다.

Keywords: