The effect of trimethylphosphate(TMP) and calciumacetate (CA) as a mic;eatomg agemt on the crystallization of PET was studied by means of nonisothermal crystallization kinetic analysis. TMP and CA were added at the stage of polycondensation reaction. Nonisothermal crystallization thermograms obtained by differential scanning calorimetry (DSC) were analyzed based on the Ozawa equation. Thermal studies clearly showed that the addition of TMP and CA resulted in decreasing the crystallization temperature obatined on heating scan from the glassy state and increasing the crystallization temperature obtained on cooling scan from the melt. The values of the Ozawa exponent n varied in the range of 1.1 to 3.9 ; non-integer values are indicative of heterogeneous thermal nucleation in the crystallization procedure.

인과 금속 화합물을 PET 중합 공정에서 첨가하여 이 화합물들이 PET의 결정화 거동에 어떠한 영향을 미치는지 확인하였다. 비등온 결정화 거동을 측정하기 위하여 DSC를 이용하였고 Ozawa 식에 의하여 그 결과를 해석하였다. 인과 금속 화합물이 증가함에 따라 무정형 고분자의 온도를 상승시켜 구한 가열 결정화 온도 (T_ch)는 감소하였고, 용용물을 냉각시키면서 구한 냉각 결정화 온도 (T(sub>cc)는 중가하였다. Ozawa 식의 지수 n은 1.1-3.9의 범위에서 변화되었는데, 이 값이 정수 값이 되지 않는 이유는 결정화 과정에서 핵의 생성이 heterogeneous하기 때문이다.

Keywords: poly(ethyleneterephthalate); crystallization; nucleating agent; Ozawa; kinetics