The thermal degradation of newly developed MMNO/cellulose pre-dope was investigated to understand the degradation mechanism of molecular weight and α-cellulose content in the processing of cellulose fiber. The effects of thermal degradation on the physical properties of fiber were also studied. The variations of molecular weight and α-cellulose content of cellulose fiber decrease by the thermal degradation depend on the basis of the dope concentration and the processing temperature. These results, the mechanism of thermal degradation in MMNO/cellulose dope was explained. The thermal degradation led to the decrease in chain orientation of cellulose fiber. It was found that this caused the reduction of fibrillation and the mechanical properties of cellulose fiber significantly.

새로운 방법에 의하여 제조된 MMNO/셀룰로오스 pre-dope를 이용한 셀룰로오스 섬유 제조시, 열분해에 따른 셀룰로오스의 분자량 및 알파 셀룰로오스 함량 변화와 이들이 셀룰로오스 섬유 물성에 미치는 영향에 대하여 고찰하였다. Dope의 열분해는 셀룰로오스 섬유 분자량 및 알파 셀룰로오스의 함량을 감소시키며 dope 농도와 열분해 온도에 따라 감소 경향이 달라지는 것으로부터 MMNO/셀룰로오스 dope의 열분해 메카니즘을 이해할 수 있었다. 열분해에 의한 분자량 저하와 알파 셀룰로오스 함량 감소는 섬유의 배향성을 낮추어 섬유의 피브릴화 현상을 감소시키고 아울러 섬유의 기계적 특성에 영향을 미침을 확인할 수 있었다.

Keywords: cellulose fiber; N-methylmorpholine N-oxide; thermal degradation; molecular weight; fibrillation