Bi-Polymer film electrodes of Polypyrrole (ppy) and Polyaniline (pan) were prepared by electrochemical implantation into Porous ppy matrix with pan as level of 10 to 35% in order to improve the electrical properties. The rate constants of electropolymerization reactions were measured with smooth Pt, Pt covered with ppy (Pt/ppy), and Pt covered with pan (Pt/pan) of modified rotating disk electrode. The electropolymerization rate of pan polymer was faster on the Pt/ppy electrode as 2.67 x 10^-5 cms^-1 by a factor of hundred than 2.30×10^-7 cms^-1 of the Pt/pan. Cyclic voltammograms of Pt/ppy/pan (x) electrodes were quite different with the doping ions which were ClO₄^- and PF₆^-. The characteristic properties of redox reaction were more obvious at doped with PF₆^- ion. The amount of Pan in the ppy matrix enhanced the doping level of the electrode to 52% at pan content (x) of 0.2, doping/undoping efficiency to 88%, and the conductivity of the ppy/pan was 331 Scm^-1 at x = 0.35. However the cyclability was reduced by 75%, relative to PPy alone.

피롤고분자(ppy)와 아닐린고분자(pan)로 된 두 성분의 고분자 복합체 전극을 전기화학적 방법으로 제작하기 위하여, 먼저 다공성 ppy피막을 백금(Pt)위에 중합한 후 그 다공성 피막내에 pan을 그 조성이 10-35%되게 끼워심기 중합하여 이 피막의 전기적 성질들을 개선시켰다. 이 때 전기적 중합속도를 Pt, Pt위에 ppy를 1.70 Ccm^-2량으로 입힌 Pt/ppy, 그리고 Pt위에 Pan을 0.1130 Ccm^-2 만큼 입힌 Pt/pan 회전판 전극들에서 측정하였다. 그 값은 Pt/ppy 전극에서 2.67×10^-5cm/s로 Pt/pan 전극의 2.30 x 10^-7cms^-1보다 백배이상 크게 나타났다. Pt/ppy/pan (x) 전극의 순환전압 전류 특성은 고분자 가닥들의 polaron자리에 도핑된 이온이 ClO₄^-일 때보다 PF₆^-일 때 더 뚜렷하였다. 아닐린고분자 함량(x)이 0.2일 때 이 피막의 도핑준위가 52%까지 증가하였으며, 도핑/탈도핑 효율은 88%였고, 전기전도도는 x가 0.35일 때 331 Scm^-1으로 ppy만일 때보다 다섯배나 증가하였다. 그러나 cyclability는 ppy만으로 된 경우에 비하여 75%까지 감소하였다.

Keywords: electropolymerization; polypyrrole; polyaniline; polymer composite; dopant