  • Ionic Conductivity of Poly(ethylene oxide)/Poly(epichlorohydrin)/LiClO4 Mixtures
  • Jun SM, Moon SI, Kim WS, Min KE
  • Poly(ethylene oxide)/Poly(epichlorohydrin)/LiClO4 복합체의 이온전도성
  • 전성민, 문성인, 김우식, 민경은
Abstract
The ionic conductivity and thermal properties of poly(ethylene oxide)/poly (epichlorohydrin) blends containing lithium perchlorate were studied. The amount of salt required for complete disruption of the PEO crystalline phase in PEG/PECH (80:20) blend was much smaller than that in the pure PEG. The ionic conductivities of the PEG-lithium salt mixtures were enhanced by adding PECH, but this was not effective at the higher content of PECH.

리튬염을 함유하는 폴리에틸렌옥시드/폴리에피클로로히드린 블렌드의 이온전도도 및 열적 성질을 조사하였다. 20wt%의 PECH를 함유하는 PEO/PECH 블렌드는 PEO 단독계에 비해 소량의 리튬염을 첨가하더라도 PEO의 결정성이 파괴됨을 확인하였으며, PECH가 첨가됨으로서 이온전도도는 증가하지만 어느 값 이상에서는 더 이상 증가하지 앉았다.

Keywords: Ionic Conductivity; Thermal Behavior; PEO/PECH Blends; Solid Polymer Electrolyte

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1998; 22(2): 275-284

    Published online Mar 25, 1998

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: