Article
  • Electrical Properties of the Plasticized Polymer Electrolytes Based on Acrylonitrile-Methyl Methacrylate(Oligo oxyethylene) Ethyl Ether Methacrylate Terpolymers
  • Kim DW, Kim YR, Sun YK, Oh BK, Moon SI, Jin BS
  • 폴리(아크릴로니트릴-메틸 메타크릴레이트-(올리고옥시에틸렌) 에틸에테르 메타크릴레이트) 삼원 공중합체를 이용한 고분자 전해질의 전기적 특성에 관한 연구
  • 김동원, 김영록, 선양국, 오부근, 문성인, 진봉수
Abstract
The electrochemical characteristics of the plasticized polymer electrolytes composed of acrylonitrile-methyl methacrylate-(oligo oxyethylene) ethyl ether methacrylate terpolymer and liquid electrolyte solution were Investigated. The encapsulation of liquid electrolyte in the matrix polymer was found to diminish the passivation of lithium electrode. The ionic conductivities of these systems reached a range of 8.7×10-4∼9.1×10-4S/cm in the presence of 70 wt% of liquid electrolyte solution at room temperature. The polymer electrolytes studied in this work were electrochemically stable up to 5.0 V vs Li.

폴리(아크릴로니트릴-메질 메타크릴레이트-(올리고옥시에틸렌) 에틸에테르 메타크릴레이트) 삼원 공중합체와 액체 전해액으로 구성된 가소화된 고분자 전해질을 제조하여 이들의 전기적 특성을 조사하였다. 고분자 전해질에 사용되는 매트릭스 고분자와 액체 전해액과의 친화성을 향상시킴으로써 전해액의 누출 현상을 개선하였으며, 전해액을 고분자 매트릭스에 효과적으로 encapsulation시킴에 따라 전해액에 의한 리튬 전극의 Passivation 현상을 크게 줄일 수 있었다. 상온에서 이온 전도도를 측정할 결과, 액체 전해액 함량이 증가함에 따라 이온 전도도는 증가하였으며, 70wt%의 전해액을 포함하는 경우, 이온 전도도는 8.7×10-4∼9.1×10-4S/cm 범위이었다. 제조된 고분자 전해질은 리튬 전극을 기준으로 하여 5.0V까지 전기화학적으로 안정한 것으로 확인되었다.

Keywords: ionic conductivity; lithium polymer battery; polymer electrolyte

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1997; 21(5): 861-870

    Published online Sep 25, 1997

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: