In this study, the effects of particle size and porosity on electromagnetic and electromagnetic wave absorbing properties of an epoxy-ferrite composite were investigated. The complex permeability, permittivity and electromagnetic attenuation value of the composite were obtained using an impedance/gain phase analyzer (HP4194A) and a network analyzer (HP8753C) in the frequency range from 1 MHz to 5 GHz. The complex permeability of the composite and the real part of permittivity increased with increasing the particle size of ferrite. The imaginary part of permittivity was independent of the particle size. The relaxation spectrum of fille complex permeability had gotten broad with increasing the porosity of composite. The particle size distribution had an effect on the complex permeability of composite. However the complex permittivity was independent of the particle size. The attenuation frequency mange could be changed by controlling the particle size and the particle size distribution of ferrite at the given ferrite content.

에폭시-페라이트 복합재료의 전자기적, 전자파 흡수 특성에 대한 입자크기 및 기공율의 효과를 분석하였다. 복합재료의 복소투자율과 유전율 및 전자파 흡수 특성은 1MHz에서 5GHz까지의 주파수 영역에서 impedance/gain phase analyzer (HP4914A)와 network analyzer (HP8753C)를 이용하여 각각 구하였다. 페라이트 입자 크기가 증가할수록 복합재료의 복소투자율은 증가하였다. 유전율의 경우 실수부는 입자 크기가 증가함에 따라 증가하고, 허수부는 입자 크기에 무관하다. 기공율이 증가함에 따라 복소투자율의 이완곡선은 완만하게 된다. 입자 크기 분포의 차이는 복소투자율에 영향을 주지만 복소유전율에는 무관하였다. 동일한 페라이트 함량의 복합재료에서 페라이트 입자의 크기 및 입자 크기 분포를 조절하면, 전자파 흡수를 나타나는 주파수 대역이 변하였다.

Keywords: particle size; complex permeability; attenuation; composite