Article
  • Polymer Alloy of PVC with Transparent ABS Resin Ⅱ : Mechanical Property
  • Lim JC, Min KE
  • 염화비닐 수지와 투명 ABS 수지에 의한 고분자 합금 II:기계적 물성
  • 임정철, 민경은
Abstract
The mechanical properties of poly(vinyl chloride), PVC, and transparent acrylonitrile-butadiene-styrene resin, Tr-ABS, blends were studied for stress-strain, flexural, and impact behavior. The blends was found to be more ductile than Tr-ABS in general, and significant stress-whitening behavior owing to the formation of shear band and craze was observed. The impact strength of the blends containing 50 to 60% of Tr-ABS by weight was almost double to the pure Tr-ABS. It was considered that brittle-ductile (B-T) trasition in failure occurs at the blends containing above the levels of 30 wt% Tr-ABS resin.

인장시험, 굴곡시험 및 충격시험을 통하여 용융혼련법으로 제조된 염화비닐 수지 (PVC)와 투명 ABS 수지 (Tr-ABS) 블렌드의 기계적 물성을 조사하였다. 인장시험 및 굴곡 시험 결과 Tr-ABS가 PVC에 첨가됨에 따라 brittle한 성질이 점차 사라지고 ductile한 성질이 증가됨을 관찰하였으며, shear band와 크레이즈의 생성에 의한 것으로 생각되는 백화현상이 증가함으로써 비편재화 변형기구에 의한 파괴가 일어남을 알 수 있었다. 또한 Tr-ABS가 30 ∼60중량% 함유된 블렌드의 충격강도는 순수한 Tr-ABS의 충격강도에 비해 현저히 증진되었으며 계에 따라 최고 100% 가까이 증가함을 볼 수 있었다. PVC/Tr-ABS 블렌드의 경우 약 30중량%의 Tr-ABS가 첨가되면 B-T(brittle-ductile)전이가 일어나는 것으로 해석되었다.

Keywords: PVC; transparent ABS; polymer alloy; mechanical property; rubber toughened plastics

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1996; 20(5): 783-790

    Published online Sep 25, 1996

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: