This paper deals with the study on the effects of lowering the curing temperature and also with the time of high temperature-curing anhydride-based DGEBA epoxy resin system for filament winding. Five curing conditions having different curing temperatures and times were selected and tested, where the final curing temperature was in the range of 120∼160℃. As the curing temperature and time increased, the mechanical and thermal properties somewhat increased. Besides the relatively low temperature curing condition( final curing temperature : 120℃ ), the other curing conditions( final curing temperature ≥ 140℃ ) were found to be adequate for the curing cycle of the present anhydride-based epoxy resin system for filament winding. The examination of fracture surfaces revealed that the more complicated fracture surface formed as the curing temperature and time increased.

본 논문은 필타멘트 와인딩 공법에서 고온경화용으로 사용되는 DGEBA-산무수물계 에폭시 수지조성의 경화온도를 낮추고 시간을 줄일 경우 그 영향을 여러가지 물성 관점에서 비교, 검토한 것이다. 최종 경화 온도가 120∼160'℃ 범위인 5종의 경화조건을 설정하여 실험하였다. 경화 온도와 시간이 증가할수록 기계적 및 열적특성은 약간 증가하는 경향을 보여주었다. 비교적 낮은 온도에서의 경화 조건(최종경화온도 : 120℃)을 제외한 나머지 경화 조건(최종경화온도≥140℃)은 필라멘트 와인딩용으로 사용되고 있는 현재의 산무수물계 에폭시 수지 조성의 경화 조건으로 적합한 것으로 판명되었다. 에폭시 수지 시편의 파단면을 관찰한 결과 경화 온도와 시간이 증가할 수록 더 복잡한 파단면이 형성되는 것을 알 수 있었다.

Keywords: epoxy resin; cure temperature; filament winding