The effects of frequency, volume fraction of ferrite, and particle size on the electric and magnetic properties of epoxy composite containing Ni- Zn ferrite were investigated. The composites were prepared by the cement mixed method and shaped as coaxial, toroidal, and disc types. The complex permeability and permittivity were obtained using an Impedance/Gain phase Analyzer(HP4194A) and a Network Analyzer(HP8753C) in the frequency range from 1 MHz to 5 GHz. The complex permeability of the composites increased with increasing the amount of ferrite. Especially the complex permeability of the composite showed the frequency dispersion chracteristic. A model to describe such phenomenon was proposed. The complex permittivity of the composite mainly depended on the volume fraction of the filler and was relatively independent on the frequency and the particle size of filler.

니켈-아연 페라이트를 포함한 에폭시 복합재료의 전기, 자기적 성질을 주파수, 조성 및 입자의 크기 함수로 분석하였다 복합재료는 cement mixed method에 의해 혼합하여 동축형, 토로이달형, 원판형으로 시편을 준비하였고, Impedance/Gain phase Analyzer(HP4194A)와 Network Analyzer(HP8753C)로 1MHz에서 5GHz의 주파수 영역에서 복소투자율과 복소유선율의 값을 얻었다. 에폭시-페라이트 복합재료의 복소투자율은 충진된 페라이트의 함량이 증가함에 따라 증가하고 주파수에 따라 분산거동을 일으켰다 이 분산거동을 설명하기 위한 모델을 제시하였다. 복합재료의 복소유전율은 주파수나 입자크기에 거의 무관하며 단지 충진재의 함량이 변화할때 이들의 값이 변화됨을 알 수 있었다.

Keywords: complex permittivity; comflex pemeability; frequency dispersion; composite