Article
  • The Effect of Anionic Surfactat Solution on the Phase Transition Behavior of Poly( N-isopropylacrylamide) Hydrogel.
  • Kim K, Shin YJ
  • 음이온성 계면활성제가 Poly(N-isopropylacrylamide) 수화겔의 상전이 현상에 미치는 영향
  • 김기훈, 신영조
Abstract
Poly(N-isopropylacrylamide)(pNIPAAm) hydrogels were prepared by radical polymerization and the effects of anionic surfactant solution on the phase transition behaviors of pNIPAAm hydrogel were studied. Swelling/shrinking ratio, phase transition temperature, change of transmittance and the phase transition energy of hydrogel were studied in a different concentration of sodium dodecylbenzenesulfonate(SDBS) solutions as a function of temperature. Swelling/shrinking ratio and the transition temperature were increased as the surfactant concentration increased. Phase transition temperature of pNIPAAm hydrogel in a pure water is 33℃∼35℃ but, it increased up to 47℃ in a 10mM of SDBS solution. On the other hand, phase transition energy was decreased from 1.56(cal/g) in pure water to 0.18(cal/g) in 10 mM of SDBS solution.

음이온성 계면활성제가 poly(N-isopropylacrylamide)(pNIPAAm) 수화겔의 상전이 현상에 미치는 영향을 조사하기 위하여 N-Isopropylacrylamide를 자유라디칼 중합에 의하여 제조하였다. 제조된 수화겔의 팽윤/수축비, 상전이 온도, 온도에 따른 투광도의 변화 및 상전이 옅량 등을 각각 다른 농도의 sodiumdodecy1benzenesulfonate(SDBS) 수용액 속에서 조사하였다. 계면활성제의 농도가 커질수록 즉, 수화겔과 화합할 수 있는 계면활성제의 자유이온의 양이 많아질수록 수화겔의 팽윤/수축비와 상전이 온도는 증가하였다. PNIPAAm 수화겔의 상전이 온도는 순수한 수용액에서 33℃-35℃이지만 10mM의 SDBS에서는 약 47℃까지 증가하였다. 상전이에 필요한 열량은 순수용액에서의 1.56(cal/g)으로 부터 10mM SDBS속에서의 0.18(cal/g)까지 감소하였다.

Keywords: poly(N-isopropylacrylamide); hydrogel; anionic surfactant

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1994; 18(5): 860-867

    Published online Sep 25, 1994

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: