Natural rubber(NR) was crosslinked with dicumyl peroxide(DP) to prepare spherical NR networks. The molecular weight between crosslinks was controlled with a DP concentraction, and ranged from 2.6×10³g/mole to 2.0×10⁴g/mole. Carbon tetrachloride, benzene, cyclohexane, n-hexane, n-decane, dichloromethane, and tolune were used as solvents in this study. The degree of crosslinking of the samples was determined using the equilibrium volume-swelling data based on the Flory-Huggins theory, and the diffusion coefficients of solvents into NR networks were calculated using a diffusion equation based on Fick's law. Results showed thats the higher the degree of crosslinking, the greater the diffusion coefficient

천연고무에 가교제인 dicumyl peroxide를 혼합한 후 이를 가교시켜 고분자 망상구조의 구형(sphere)시편을 준비하였다. Dicumyl peroxide의 첨가량을 변량시켜 시편의 가교점간 분자량 (M_c)을 2.6×10³g/mole에서 2.O×10⁴g/mole까지 변화시켰다. 본 확산실험에 적용된 용제의 종류는 carbon tetrachloride, benzene, cyclohexane, n-hexane, n-decane, dichloromethane, 그리고 toluene이었다. 시편의 가교도는 Flory-Huggins이론에 근거한 평형부피팽윤값으로부터 결정하였으며, 가교시편에 대한 용제의 확산계수는 Fick의 확산법칙을 이용하여 결정하였다. 용제의 확산계수는 천연고무망상의 가교도가 높을수록 상승하는 경향을 보여주었다 외삽에 의해서 추정한 가교도가 극도로 낮은 천연고무에 있어서의 용제의 확산계수(D_o)는 천연고무와 용제간의 상호작용 파라미터값(χ)에 대해서 D_o∼χ^1.8 관계식에 의존하였다. 용해성 파라미터(δ₁)가 각각 다른 용제에 의한 천연고무망상의 평형팽윤비로부터 천연고무의 δ₂값을 결정하였으며 그값은 17.5 MPa^1/2이었다. 이성분 용제혼합물에 의한 팽윤거동에 있어서 초기팽윤시간에는 χ값이 상대적으로 낮은 용제의 선택적 홉수가 관찰되었다.

Keywords: