For the preparation of supported TiCl₄ catalysts, MgCl₂ was dissolved in ethanol, i-butanol or 2-ethyl-1-hexanol(EHA) and used as solution pr after precipitaion. The effects of various preparation conditions on catalyst behaviors have been studied for propylene polymerization. EHA solvent gave highesl. activity and n-hexane diluent showed advantages for not only easy handing but high activity. MgC1₂ dissolved in ethanol could be precipitated with n-hexane and the catalyst prepared from reprecipitated MgCl₂ improved its activity and isospecificity. Retreatment of prepared catalyst with TiCl₄ resutlted in high activity as well as stereoregularity and 1,2-dichloroethane was a suitble washing medium for high stereogularity

Ethanol(EtOH), 2-methyl-1-propanol(i-BuOH), 2-ethyl-1-hexanol(EHA) 등을 Mgcl₂의 용매로 사용하고 용액상 또는 침전상으로 담지 TiCl₄중합촉매를 제조하여 프로필렌을 중합할 때에, 촉매제조 조건 즉 알코올의 종류, 용제인 xylene과 n-hexane, 반응온도, TiC1₄ 재처리, 촉매세척 등이 촉매의 활성과 입체규칙성에 미치는 영향을 조사하였다. MgCl₂용매로 EHA를 사용하였을 경우에 가장 큰 촉매활성을 나타내었으며, n-hexane으로 MgCl₂용액을 묽혀 주는 것이 촉매제조상의 용이함 뿐만 아니라 활성증가의 면에서 유리하였다. EtOH에 용해된 MgCl₂는 n-hexane으로 침전되고 재침전된 MgCl₂에서 얻은 촉매의 활성과 입체규칙성이 향상되었으며, 용제로 xylene을 사용하는 것이 촉매제조에 편리하였다. MgCl₂를 용액상으로 TiCl₄와 반응시켜 촉매를 제조할 경우에 저온에서 얻은 촉매의 활성과 입체규칙성이 우세하였으나, 침전상으로 반응하여 얻은 촉매의 거동은 반응온도에 거의 무관하였다. 제조한 촉매를 TiCl로 재처리하면 활성과 입체 규칙성이 향상되었으면, 촉매의 세척제로 1,2-dichloroehane을 사용하면 입체규칙성이 증가되었다.

Keywords: