  • The Effect of SBR Photografted Silica Gel on the Physical Properties of Rubber Compounds and the Adhesion between Steel Cord and Rubber
  • Chae KH, Cho DW, Choi MH, Kim JM, Oh S
  • SBR로 광그라프트된 실리카겔이 고무물성 및 고무-강선간의 접착에 미치는 영향
  • 채규호, 조덕원, 최민호, 김재문, 오세철
Abstract
The initial physical properties of rubber compounds containing SBR photografted silica gels showed increased hardness and modulus, but tensile strength and elongation at break did not so much changed compared with the compounds containing ordinary silica gel. Similar results was obtained after thermal aging at 90℃ for several days. There was no difference of rubber-steel cord adhesion force between the rubber compounds containing ordinary silica gel and SBR photografted silica gel before aging. However adhesion force, rubber coverage, and breaking energy between rubber and steel cord lasted longer after aging. These results show that the compounds containing SBR photografted silica gel have the properties of improved resistance on thermal aging of adhesion between steel cord and rubber.

styrene-butadiene 고무(SBR)로 광그라프트된 실리카겔 고무혼합물의 초기 물성은 보통의 실리카겔을 사용하였을 경우에 비하여 경도, 탄성율은 중가하였으나 인장강도, 신율등의 물성은 별 차이가 없었으며 90℃에서 수일간 열노화 시킨 후에도 같은 결과를 얻었다. 또한 SBR로 광그라프트된 실리카겔의 고무혼합물은 보통의 실리카겔을 사용한 경우에 비하여 노화 전에는 고무-강선간의 접착력에 별 차이가 없었으나 90℃에서 9일간 열노화시킨 후에는 고무-강선간의 접착력, 신율, 고무부착율이 현저히 증가하였다. 이와같이 SBR로 광그라프트된 실리카겔은 고쭈-강선간의 노화에 대한 내구력을 향상시키는 특성이 있다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1994; 18(3): 330-337

    Published online May 25, 1994

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: