Naphthalimidoethylmethacrylate(NIEM) and naphthalimidobutylmethacry1 ate(NIBM)were copolymerized with styrene (ST) using : azobisisobutyronitrile as an initiator in dimethylformamide at 60℃, respectively. The compositions of the copolymers were analyzed by ultra-violet spectrophotometry. The monomer reactivity ratios for the systems and Alfrey-Price's resonance effect(Q) and polar effect(e) values for NIEM and NIBM were determined as follows : NIEM(1)-ST(2) r₁=0.28, r₂=0.36, Q₁=0.84, e₁=0.72 HIBM(1)-ST(2) r₁=0.29, r₂=0.40, Q₁=0.78, e₁=0.67 The product of r₁ and r₂ suggests that poly(NIEM-co-ST) and poly(NIBM-co-ST) have a greatly alternating tendency. The copolymers were observed to exhibit a monomer emission band at 380 nm and an excimer emission band at 460 nm. The ratios of the excimer to the monomer emission intensities of poly(NIBM-co-ST) were higher than those of poly(NIEM-co-ST). The tendency for the copolymers agreed with that for poly(NIEM)and poly(NIBM) in our previous paper.

60℃에서 디메틸포름아미드중에서 아조비스이소브틸로니트릴을 개시세로 사용하여 나프탈이미도에틸메타크릴레이트 (NIEM) 및 나프탈이미도부틸메타크릴레이트(NIBM)를 스티렌(ST)과 각각 공중합하였다. 공숭합체의 조성은 자외선분광광도법으로_분석하였다. 공중합의 단량체 반응성비와 NIEM 및 NIBM의 공명효과(Q) 및 극성효과(e)를 구하였다. NIEM(1)-ST(2) r₁=0.28, r₂=0.36, Q₁=0.84, e₁=0.72 NIBM(1)-ST(2) r₁=0.29, r₂=0.40, Q₁=0.78, e₁=0.67 r₁과 r₂의 곱은 NIEM-ST 공중합체와 NIBM-ST공중합체가 큰 교호성을 가지는 것을 시사한다. 이들 공중합체는 380nm에서 단량체발광띠와 460nm에서 엑시마발광띠를 나타내었다. NIBM-ST공합체의 단량체발광강도에 대한 엑시마발광강도비는 NIEM-ST 공중합체의 그 비보다 컸다. 공중합체에 대한 이 경향은 이전 연구에서의 poly(NIEM)과 poly(NIBM)의 경향과 일치하였다.

Keywords: