  • Studies on the Styrenic Polymer 2.Synthesis of Styrene/Acrylonitrile/N-Phenylmaleimide Terpolymer and Properties of Modified ABS
  • Ahn TO, Kil YS, Park LS
  • Styrenic Polymer 연구 2. Stryene/ Acrylomitrile/ N- Phenylemaleimide Terpolymer의 합성 및 개질 ABS의 물성
  • 안태완, 길유성, 박이순
Abstract
To enhance the heat resistance of acrylonitrile-butadiene-styrene(ABS), the matrix part(SAN) was modified by introducing N-phellylmaleimide(PMI) monomer, Styrene-acrylonitrile(AN)-PMI terpolymer was synthesized by the semi-continuous emulsion polymerization method with varying PMI content while keeping styrene/AN ratio at 75/25. PSAN terpolymer was blended with g-ABS rubber part utilizing twin screw extrucler to get modified ABS. Modified ABS sample(PSAN : g-ABS= 70 : 30) showed increased thermal stability, hardness, and tensile strength with increasing amount of PMI in the PSAN terpolymer. The impact strength, however, showed maximum at PMI content of 15 wt.% in PSAN. This behavior could be explained by investigating the miscibility of PSAN and shell part of g-ABS(i. e. SAN 25)

ABS수지의 내열성을 증가시키기 위하여 매트릭스인 SAN고분자 주쇄에 고리 구조를 가진 N-phenylmaleimide(PMI) 단량체를 도입하였다. 즉 styrene과 acrylonitrile(AN)의 무게비를 75 : 25로 도정시키고, PMI의 양을 변화시키면서. 삼원 공중합체(PSAN)을 반 연속 유화 중합법으로 합성하였다. 합성된 PSAN은 그라프트 ABS고무(g-ABS)와 용융 블렌드하여 내열성의 향상 및 기계적 성질과의 관계를 조사하였다. 개질 ABS수지(PSAN : g-ABS=70 : 30)의 내열성. 경도 및 인장강도는 PMI의 함량이 증가할수록 증가하였으나 내충격성은 PSAN중 PMI함량이 l5wt%일 때 최대를 나타내었느며 이것을 PSAN 매트릭스와 고무 성분중 SAN 부분과의 상용성 관계를 조사하여 해석하였다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1993; 17(4): 357-364

    Published online Jul 25, 1993

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: