Structural and morphological behavior of solution grown nylon 4,6 crystals has been determined and compared with other polyamides, especially nylon 6,6. The lath shaped crystallization products, aggregated in the form of sheaves, possessed the characteristics of chain folded single crystals. The measured layer thickness by small angle X-ray diffraction varied with crystallization temperatures. The dependence of the layer thicknesses on the crystallization temperatures showed a horizontal plateau followed by a monotonous increase with the high crystallization temperature(T_C ) of about 130 ℃. The comparison of wide and small angle : X-ray reflections combined with the examination of electron diffraction patterns of sedimented mat of crystals shows that the chains in the nylon 4,6 are perpendicular to the lamellar surface and the 001 planes are inclined to the fold surface, which are quite contrast to other polyamides where tile chains are inclined to the lamellar surface and the 001 planes are parallel to the fold surface.

여러 온도의 용액상태하에서 Nylon 4,6을 결정화시킨 다음 그들의 형태학적 거동과 결정구조를 해석하였다. 결정산물은 판상형(lath-Shaped)의 격정들이 나뭇단(sheaves) 모양의 형태로 뭉쳐서(aggregated) 나타나고 있었으며, 결정내부는 사슬이 규칙적으로 굴곡된 라멜라(chain folded lamellae) 형태를 취하고 있음이 광각(wide angle) 및 소각 X-선 회절(small angle X-ray diffraction) 그리고 투과 전자현미경(transmission electron microscopy)에 의해 확인되었다. 라멜라의 두께는 진공하에서 용매를 완전히 제거시킨 후 소각 X-선 회절에 의해 측정되었으며 결정온도에 따라 변화하는 양상을 보였다. 결정온도에 따른 라멜라의 두께늑 약 130 ℃ 이하의 결정온도에서는 일정한 값을 유지하였으나 그 이 상의 온도에서는 단조증가(monotonous increase)하는 현상을 나타내었다. 또한, Nylon 4,6의 결정내력에 사슬들은 라멜라 표면(fold surface)에 수직하게 배열(perpendicular chain packing)되어 있었으며 이것은 Nylon 6.6과 같은 여타 폴리아미드의 경우 사슬이 라멜라 표면에 기울어져(inclined chain packing) 배열되어 있는 현상과 가장 두드러진 결정구조상의 차이점을 나타내 고 있다.

Keywords: