The complex Young's modulus, E^*, and the complex strain-optical coefficient, O^*, of a conventional amorphous polyarylate were studied around the glassy-to-rubber transition zone. Measurement were performed over the frequency range of 1 to 130 Hz at various temperature between 205℃ and 255℃ and the master cures were constructed with the time-temperature superposition principle. The E^* of polyarylate showed typical relaxation behavior of amorphous polymers. The rubbery plateau modulus, E_N'=11.2MPa, was higher than the value of common amorphous polymers. The O^* of polyarylate was positive over the whole reduced frequency range. A modified stress-optical rule(M-SOR) proposed previously was applied; by comparing E^* with O^*, the E^* could be separated into two component functions, E_R^* and E_G^* and they allowed the consideration of relaxation mechanism responsible for the complex modulus. The stress-optical coefficients, C_R and C_G, corresponding to E_R^* and E_G^* were 6.8×10^-9 Pa^-1 and 2.0×10^-11Pa^-1, respectively. The temperature dependence of the shift factors used in constructing master curves of E^*, O^*, E_R^* and E_G^* was discussed.

무정형 폴리아릴레이트에 대해, 고무상 영역에서 유리상 영역에 걸쳐 동적 탄성율, E^* 및 동적스트레인-광탄성 계수, O^*를 측정하여 고찰하였다. 측정은 205℃에서 255℃ 사이의 여러 온도에 대해, 주파수를 1∼130 Hz로 변화시키며 행하였고, 시간-온도 환산칙을 적용하여 E^*, O^*의 마스타 곡선을 합성하였다. 구성한 두 특성치의 주파수 스펙트럼에 대해, 이전에 우리가 제안한 수정 응력-광탄성칙을 적용하여 고찰하였다. 폴리아릴레이트의 동적 탄성율 E^*는 전형적인 무정형 고분자의 특성을 보였으며, 고무 평단 영역의 탄성율, E_N'이 다른 고분자에 비해 매우 큰 11.2MPa을 나타냈다. 동적 스트레인-광탄성 계수 O^*는, 페닐기가 측쇄로 존재하는 고분자들에 비해 매우 억제된 주파수 의존성을 보였다. 또한 측정된 전 영역에서 양의 값을 보였다. 수정 응력-광탄성칙에 의해 구한 폴리아릴레이트의 응력-광탄성 계수, C_R, C_G는 각각 6.8×10^-9Pa^-1과 2.0×10^-11Pa^-1을 나타냈다. 결정된 광탄성 계수를 이용하여, 측정한 영역에서의 동적 탄성율 E^*를, 성분 탄성율 E_R^*, E_G^*로 분리하여, 각탄성율의 발생기구에 대해 고찰하였다. 또한 마스타 곡선 합성시 사용한 각 특성치의 환산이동인자의 온도 의존성에 대해서도 고찰하였다.

Keywords: