Tensile and dielectric properties of short aramid or carbon fiber reinforced chlorosulfonated polyethylene(CSM) composites were investigated. The composites were prepared by the mill-mixing method. The effects of vulcanization, fiber types and contents on the tensile strength, dielectric loss tangent(tan δ), specific inductive capacity(ε_r), and volume resistivity were discussed. The short fiber reinforced CSM composites showed better tensile and dielectric properties when CSM matrix was vulcanized. Tensile properties of the CSM composites with or without vulcanization were affected by the fiber types and the effect was larger in case of the aramid fiber reinforced composites. The tan δ and ε_r were affected by the fiber types and contents in the unvulcanized CSM composites, whereas those dielectric properties increased with fiber contents regardless of fiber types in the vulcanized CSM composites. It was observed that the volume resistivities of the CSM composites were almost same as that of the CSM matrix regardless of fiber types and contents.

Mill-mixing 방법으로 제조된 단섬유 강화(Aramid fiber, Carbon fiber) Chlorosulfonated Polyethylene(CSM) 복합 재료의 미가황 상태와 가황 상태에서의 인장 강도와 유전 정접(Tan δ), 비유전율(ε_r), 체적 저항을 연구하였다. 가황시킨 복합 재료는 미가황 상태에서의 단섬유 강화 복합재료보다 더 좋은 인장 강도와 유전 성질을 보임을 알 수 있었다. 복합 재료의 인장 강도는 미가황 상태와 가황 상태에 따라 다른 단섬유 종류의 영향을 보였으며 Aramid 단섬유가 더 큰 영향을 받는 것으로 나타났다. 단섬유의 종류에 관계없이 미가황 상태 복합 재료의 Tan δ와 ε_r는 단섬유 함량의 영향이 거의 없었으나 가황 상태 복합 재료의 Tan δ와 ε_r는 단섬유 함유량이 증가함에 따라 증가하였다. 복합 재료의 체적 저항은 단섬유의 종류와 함량에 관계없이 CSM 기질의 그것과 거의 같은 값(10¹³∼10¹⁵Ωcm)을 가졌다.

Keywords: