The copolymerization of ethylene and 1-hexene with MgCl₂/EHA/TiC1₄-TEA catalyst system in hexane has been studied in which MgCl₂ was dissolved in 2-ethyl-1-hexanol(EHA). In the catalyst preparation, mole ratio of MgCl₂/EHA was fixed to be 1/6 and reaction temperature and time were 30℃ and 2h, respectively. The effects of catalyst retreatment with TiC1₄, mole ratio of catalyst components, feed ratio of monomers and addition of Lewis bases, diisobutylphthalate(DIBP) and phenyltriethoxysilane(PTES), on the activity and composition of copolymers have been investigated. For ethylene/1-hexene copolymerzation, activity increased with (TEA)/[Ti] (>25) and 1-hexene content gave a maximum at [TEA]/[Ti]=100. With addition of Lewis bases, the activity and 1-hexene contents in copolymer decreased. The reactivity ratios obtained by Kelen-Tudos method were r_E=53.8, r_H=0.18 for MgCl₂/EHA/DIBP/TiC1₄-TEA/ catalyst system and r_E=70.8, r_H=0.08 for MgCl₂/EHA/DIBP/TiC1₄-TEA/PTES catalyst system. Thermal and mechanical properties of copolymer were also investigated with 1-hexene contents.

염화마그네슘을 2-Ethyl-1-hexanol(EHA)에 녹인 용액으로부터 제조한 사염화티탄 담지촉매로 에틸렌/1-헥센 공중합체를 합성하였다. 이때 촉매의 제조에서 MgCl₂/EHA의 몰비는 1/6, 반응온도는 30℃, 반응시간은 2시간으로 고정하였다. 촉매의 TiC1₄ 재처리 및 중합조건 즉 촉매성분 농도비, 단량체의 공급비 등에 따른 촉매의 활성과 공중합체의 조성을 조사하였으며, 아울러 Lewis 염기인 diisobutylphthalate(DIBP) 및 phenyltriethoxysilane(PTES)의 영향도 조사하였다. 에틸렌/1-헥센 공중합시는 (TEA)/[Ti]의 농도가 증가할수록 활성은 증가하였고 [TEA]/[Ti]=25이하에서는 중합이 되지 않았다. 그리고 공중합체의 1-헥센의 함량은 [TEA]/[Ti]의 농도비가 100에서 최대를 나타내었다. Lewis염기를 첨가함에 따라 촉매의 활성과 1-헥센의 함량은 감소하였으며, Kelen-Tudos 방법으로 구한 단량체의 반응성비는 MgCl₂/EHA/DIBP/TiC1₄-TEA/PTES 촉매계에서는 각각 r_E=70.8, r_H=0.08 이었다. 1-헥센의 함량에 변화에 따른 공중합체의 열적 및 기계적 성질도 조사하였다.

Keywords: