'Radical copolymerization of vinly acetate(VAc) and phenyl acrylate(PA) was carried out with AIBN as an initiator in benzene at 60℃ in a batch reactor. The copolymer compositions were analyzed by UV spectrophotometry. The monomer reactivity ratios, r_l (VAc) and r₂(PA) were determined by the Kelen-Tudos method ; r_l=0.22, r₂=2.48. The φ factors of the copolymer over the entire VAc compositions ranged from 0.()2 to 11.56. The φfactors of the VAc-PA copolymer increased with increasing PA compositions. The rate of copolymerization and monomer reactivity ratios of VAc and PA were compared with those obtained from VAc and vinly benzoate(LBz). It was found that the VAc-PA copolymer system has more alternating tendency than the VAc-VBz copolymer system by statistical analyses and reactivity values.

회분식 반응기를 사용하여 비닐 아세테이트(VAc)와 페닐아크릴레이트(PA)를 벤젠에서 AIBN을 개시제로 사용하여 60℃에서 라디칼 공중합을 하였다. 자외선 흡수 분광법으로 공중합체 조성을 분석하였으며, 단량체 반응성비 r_l(VAc)과 r₂(PA)든 Kelen-Tudos 방법으로 결정하였다 ; r_l=0.22, r₂=2.48. 공중합체의 φ값은 VAc의 전조성에 걸쳐 0.02∼11.56 범위의 값을 가졌고, 공중합체내의 PA조성이 증가할수록 φ값은 증가하였다. VAc와 PA의 반응성. 공중합속도 등을 VAc와 비닐벤조에이트(VBz)의 반응성, 공중합속도 등과 비교 검토하였다. 통계적인 분석과 반응성 검토 결과 VAc와 PA공중합체는 VAc와 VBz공중합체보다 더 많은 교호구조를 가지는 것으로 밝혀졌다.

Keywords: