The chelating resins containing three amidoxime groups per repeating unit of polymer were prepared from chloromethylated AN-STR copolymer beads. The AN-STR copolymers were synthesized by suspension polymerization in the presence of toluene as a diluent. The influences of diluent content and degree of crosslinking on the adsorption capacity of chelating resin for heavy metal ions were examined using with AA or ICP-AES. The chelating resin that was synthesized from AN/STR=1.25(by molar ratio), 7wt% of DVB and 120vol% of toluene showed highest adsoption capacity for Cu(Ⅱ). And the order of adsorption capacity of the chelating resin at optimum pH was Hg(Ⅱ)>Cu(Ⅱ)>UO₂(Ⅱ)>Pb(Ⅱ)>Cr(Ⅵ)>Cd(Ⅱ). The adsorption capacity of the chelating resin was greatly affected by co-existing metal ions.

현탁중합으로 가교된 AN-STR의 공중합체를 제조한 다음 클로로메틸화, 시안화, 아미드옥심화하여 중합체의 단위구조당 3개의 아미드옥심기를 배위자로 가지는 킬레이트수지를 제조하고 가교결합체의 양, 희석제의 양과 모노머의 몰비가 중금속이온의 흡착에 미치는 영향을 AA 또는 ICP-AES로 조사하였다. 중금속이온의 흡착을 위한 최적합성조건은 AN/STR의 몰비를 1.25, DVB의 양은 모노머의 7wt%, 희석제는 모노머의 80vol%로 할 때이었으며, 합성된 킬레이트수지의 중금속이온 흡착량은 최대흡착량을 나타내는 pH에서 Hg(II)>Cu(II)>UO2(II)>Pb(II)>Cr(VI)>Cd(II)의 순이었다. 또한 킬레이트수지의 중금속이온 흡착량은 공존이온에 의해 많은 영향을 받았다.

Keywords: