Interpenetrating polymer networks(IPUs) of hydrophilic polyurethane(PU) and hydrophobic polystyrene(PS) were prepared by simultaneous polymerization method. The hydrophilicity of IPNs was controlled by varying the PU composition. The surface morphology of these samples was observed with scanning electron microscope(SEM), and the wettability of the surfaces was evaluated by the contact angle measurement. The blood compatibility was estimated by in vitro platelet adhesion test and ex vivo rabbit A-A shunt test. The surface morphology of PU/PS IPNs exhibited microphase-separated structures with have the dispersed PS domains in the continuous PU matrix. In the case of the PU and PS homopolymers, significant degree of platelet adhesion and aggregation was observed. However, the platelet adhesion and deformation were suppressed on the surfaces of PU/PS IPNs. In the rabbit A-A shunts test, antithrombogenicity was assessed with the occlusion time measurement. The occlusion time of the IPN containing 60wt% of PU was 100min. This value was twice longer than of the PU control(50min), indicating the enhanced blood compatibility. From these results, it was concluded that the hydrophilic-hydrophobic IPN of the microphase-separated structure shows promising antithrombogenic activities by suppressing adhesion and activation of platelets.

친수성 폴리우레탄(PU)과 소수성 폴리스티렌(PS)으로 구성된 상호침투하는 고분자구조(IPN)를 동시중합방법에 의하여 합성하였다. 두 성분의 조성비를 변화시킴에 의하여 친수성의 정도를 조절하였다. 이들의 표면 몰폴로지는 SEM으로 관찰하였고 표면의 젖음성은 접촉각측정에 의하여 구하였다. 혈액 적합성은 in vitro 혈소판 점착실험과 토끼를 이용한 ex vivo A-A shunt 실험을 행하여 평가하였다. 합성한 모든 IPN은 폴리우레탄 matrix에 폴리스티렌이 상(domain)을 이루는 친수성-소수성 미세 상분리구조를 보였다. 혈소판 점착 실험 결과 친수성-소수성 PU/PS IPN 표면에서 순수한 폴리우레탄 및 폴리스티렌 표면보다 혈소판의 점착 및 형태 변화가 현저하게 감소하였다. A-A shunt 실험에 의한 폐색(occlusion)시 간은 IPN(PU 60wt%)이 100분으로 control로 사용한 폴리우레탄의 50분에 비하여 2배 정도 연장되는 향상된 항응혈성을 보였다. 따라서 친수성-소수성 미세 상분리구조를 갖는 IPN은 혈소판 점착 및 변형을 억제함으로써 순수한 친수성, 소수성 표면보다 우수한 혈액 적합성을 나나내었다.

Keywords: