Toughened nylon 6 was made by blending nylon 6 with a modified elastomer(SBS triblock copolymer). Impact strengths of the nylons were measured. Scanning electron microscope(SEM) and transmission electron microscope(TEM) were used to investigate the size and state of the dispersed phase. Rubber was functionalized by mixing of maleic anhydride (MA) with melt state of nylon 6 in a twin screw extruder in the presence of an initiator. Impact strength of rubber toughened nylon 6 increased with the amount of added rubber, and with uniformity of dispersed phase. Subinclusion of nylon in the rubber phase was observed from TEM micrograph. The subinclusion amount was relatively small and decreased with MA amount. Toughening mechanism of the blends of nylon 6 and functionalized rubbers was reconsidered by analyzing the experimental data.

기능화 된 SBS 트리 블록 공중합체를 분산된 탄성체상으로 사용하여 강화된 나일론 6의 기계적 성질(충격강도)을 측정하였으며 분산상의 상태 및 크기를 주사 현미경과 투과 현미경을 사용하여 관찰하였다. 탄성체의 기능화는 maleic anhydride(MA)를 사용하여 용융상태에서 반응시켜 얻었다. 나일론의 내충격성은 기능화 된 고무의 첨가량에 따라, 또 입자 크기가 균일할수록 증가하였다. 투과 현미경의 사진으로부터 일부 고무입자내에 나일론의 재함유되어 있는 것을 발견하였으나 그 양은 비교적 적었고 첨가된 MA 가 증가할 수록 감소하였다. 강화된 나일론6의 기계적 성질 데이터로부터 분산된 고무입자의 성질과 나일론6의 강화기구와의 관계를 고찰하였다.

Keywords: