Aromatic liquid crystalline polyesters were synthesized by solution polymerization from terephthalic acid/p, p'-biphenyl dicarboxylic acid(75/25 by mole%), hydroquinone(HQ) and a, ω-bis(4-hydroxy phenoxy)alkane(BIS-n) with various length of flexible spacers(n=6∼9). Effects of HQ/BIS-n ratio(by mole%) on the properties of polymers were investigated with DSC, TGA, cross-polarized microscopy, and X-ray diffractometer. The textures of polymers changed depending on the number of methylene units. The polymers with n=6 formed smectic phase, while those of n=7 showed nematic one. Transition temperatures of liquid crystalline polymers in this study showed typical oddeven effects. Thermal stabilities of polymers decreased with increase of BIS-n content.

p, p'-비페닐 디카르본산과 테레프탈산의 양이 1 : 3인 기본구조에 메틸렌의 수(n)가 6∼9인 α, ω-비스(4-히드록시 페녹시)알칸(BIS-n)을 가하여 용액중합법으로 액정 폴리에스테르를 제조하였다. 합성한 중합체의 유연쇄 도입에 따른 열적성질은 DSC, TGA로 조사하였고, 형성하는 액정상은 편광현미경으로 확인하였다. 액정상은 n에 따라 변하여 n이 6인 것은 스멕틱상을, n이 7인 것은 네마틱성을 나타내었고 합성한 중합체 T_m과 T_i는 뚜렷한 짝수-홀수 효과를 나타내었다. 또한 중합체의 열안정성은 중합체중의 Bis-n의 양이 증가할수록 저하되었다.